Nestled in the heart of Manama’s bustling industrial landscape, Junaid Metals has established itself as a trusted partner for quality materials. We take pride in supplying a comprehensive range of stainless steel products, including the exceptionally resilient Stainless Steel 1.4122 bars. Known for its outstanding durability, this grade is a cornerstone for industries that demand materials capable of withstanding challenging environments, making it a premium choice for engineering and manufacturing applications where failure is not an option.
The strength of 1.4122 stems from its thoughtful composition, which includes a significant amount of chromium for corrosion resistance and a boost of carbon for enhanced hardness. This martensitic stainless steel can be heat-treated to achieve impressive mechanical properties, offering high tensile strength and excellent wear resistance. It holds its edge superbly, maintaining its structural integrity even under substantial stress, making it far more robust than standard stainless steels for demanding tasks.
Length : 1 To 6 Meters, Custom Cut Length
Round bar : Diameter: 3mm~ 800mm
Angle bar : Size: 3mm* 20mm* 20mm~ 12mm* 100mm* 100mm
Square bar : Size: 4mm* 4mm ~100mm* 100mm
Flat bar : Thickness: 2mm ~ 100mm / Width: 10mm ~ 500mm
Hex bar : Size: 2mm ~ 100mm
Form : Round, Square, Hex(A/F), Rectangle, Billet, Ingot, Forging Etc
Surface Finishing : Pickled, Black, Bright, Polishing, Blasting, etc
Test Reports : SGS, BV, API, BSI, GHC.
Packing : Each steel bar has the singal, and several will be bundled by weaving bag or as per requirement.
Specials : Sizes and Specifications other than above can be manufactured on request
| Grade | C | Si | Mn | P | S | Cr | Mo | N | Others |
| SS 1.4122 | 0.33-0.45 | max 1.00 | max 1.5 | max 0.040 | max 0.015 | 15.5-17.5 | 0.80-1.30 | max 1.00 | – |
| Yield Rp0.2 (MPa) | Tensile Rm (MPa) | Impact KV/Ku (J) | Elongation A (%) | Reduction in cross section on fracture Z (%) | As-Heat-Treated Condition | Brinell hardness (HBW) |
| 869 (≥) | 926 (≥) | 41 | 44 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 |
| EN | DIN | AFNOR |
| 1.4122 | 1.4122 – X 39 Cr Mo 17 1 | Z 38 CD 16-01 |
Yes, Stainless Steel 1.4122 bars can be recycled after use. Stainless steel is highly recyclable, retaining its properties and reducing environmental impact, making it a sustainable material for reuse.
Yes, Stainless Steel 1.4122 bars can be welded. It is weldable using standard methods like TIG or MIG welding, though pre-heating and post-weld heat treatment may be required for optimal results.
Yes, Stainless Steel 1.4122 bars can be heat treated. It can be hardened through quenching and tempering processes, improving strength and wear resistance while maintaining its corrosion resistance properties.
This unique combination of hardness and corrosion resistance makes 1.4122 bars incredibly versatile. You’ll frequently find them machined into essential components like shafts, valves, and pump parts for the oil and gas sector. They are also the ideal choice for high-wear items such as molds, surgical instruments, and cutting tools. Essentially, any application that requires a material that won’t easily degrade under pressure or abrasive conditions is a perfect fit for the reliable performance of 1.4122 stainless steel bars.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Junaid Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Manama, Bahrain